PCE-5000 is a portable hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

The UCI hardness tester PCE-3000UL can be used for quickly checking the hardness of components even after installation, two probes are included. The device offers a wide measurement range, easy handling, robust design, and a temperature resistance up to 40 °C (104 °F). Measures hardness in Rockwell, Brinell and Vickers, the UCI hardness tester can test the tensile strength of steels up to 1740 MPa or 70 HRC. The tester comes with two probes, one UCI probe for non-destructive testing and one Leeb probe for rebound testing.

- Non-destructive hardness testing
- Ultrasonic + Leeb hardness test method
- Ideal for thin metals, complex shapes, hardened layers, or requiring very small indentation
- Fast measurement times with very high accuracy
- 2 probes for UCI and Leeb rebound testing

PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

The UCI metal hardness tester PCE-3000UL can be used for quickly checking the hardness of components even after installation, two probes are included. The device offers a wide measurement range, easy handling, robust design, and a temperature resistance up to 40 °C (104 °F). Measures hardness in Rockwell, Brinell and Vickers, the UCI metal hardness tester can test the tensile strength of steels up to 1740 MPa or 70 HRC. The tester comes with two probes, one UCI probe for non-destructive testing and one Leeb probe for rebound testing.

- Non-destructive hardness testing
- Ultrasonic + Leeb hardness test method
- Ideal for thin metals, complex shapes, hardened layers, or requiring very small indentation
- Fast measurement times with very high accuracy
- 2 probes for UCI and Leeb rebound testing

PCE-5000 is a portable hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available