PCE-5000 is a portable hardness tester or durometer that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys to measure on a minimum material thickness of 2 mm / .08 in. The test instrument can be mounted on a test stand (as an option) for series measurement in manufacturing process checking. Non-destructive testing produces microscopic indentation.

• Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
• Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
• Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
• Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
• Memory size: 1,000 groups for measurement data and 20 groups for calibration data
• Different probe types (also automatic motorized probes) available

The Ultrasonic Contact Impedance (UCI) durometer PCE-3500 has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces.

• 50 Newtons UCI probe / 11.2 lbf force, 10 and 98 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting

PCE-HT 225E is a durometer, also called a concrete rebound hammer or Swiss hammer, used for non-destructive measurements of surface hardness and compression strength. Suitable for use with concrete, rock and building materials, this rebound hammer features a direct digital display, voice functionality, USB port data interface and memory for storing up 200 measurement values.

• Test range: 10 … 60 MPa or 100 … 600 kg/cm² / 1450.38 … 8702.26 psi
• Impact energy: 2.207 J or N-m / 0.225 kgf.m / 1.6278 ft-lb or Type N
• Impact stroke: 75 ± 0.3 mm / 2.95 ± 0.012 in
• Radius of spherical tip: 25 ± 1 mm / 0.99 ± 0.04 in
• Data processing software included

The Ultrasonic Contact Impedance (UCI) durometer PCE-3500 has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces and nitrided surfaces.

• 10 Newtons UCI probe / 2.2 lbf force, 50 and 98 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting

The Ultrasonic Contact Impedance (UCI) durometer PCE-3500 has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces and nitrided surfaces.

• 98 Newtons UCI probe / 22 lbf force, 10 and 50 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting

The durometer PCE-2900 has been developed for hardness measurements on metallic materials. The durometer PCE-2900 measures the material hardness in Vickers, Brinell, Rockwell, Leeb and Shore. The durometer PCE-2900 measures the hardness according to the Leeb rebound principle. 

• Measurement according to Leeb Rebound method
• Measurement units: HLD, HRA, HRB, HRC, HB, HV, HS
• Measurement ranges: 170-960 HLD, 59.1-88 HRA, 3.5-101.7 HRB, 17.9-69.5 HRC, 19-683 HB, 80-1042 HV, 30.6-102.6 HS 
• Accuracy: ± 0.5%, Repeatability: ± 0.6%
• Impactor: Type D
• USB and WiFi for data transmission

The durometer is an analog measuring device to determine concrete strength. The measuring method of the concrete durometer is based on the Schmidt principle. With this measuring method, a kinetic impact energy hits the concrete from the durometer. The resulting rebound enables the durometer to determine the strength of the concrete.

• Nominal kinetic energy: 4.5 J
• For high-strength concrete
• Simple and quick operation
• For determining concrete hardness
• Schmidt principle

The durometer PCE-2900 has been developed for hardness measurements on metallic materials. The durometer PCE-2900 measures the material hardness in Vickers, Brinell, Rockwell, Leeb and Shore. The durometer PCE-2900 measures the hardness according to the Leeb rebound principle. 

• Measurement according to Leeb Rebound method
• Measurement units: HLD, HRA, HRB, HRC, HB, HV, HS
• Measurement ranges: 170-960 HLD, 59.1-88 HRA, 3.5-101.7 HRB, 17.9-69.5 HRC, 19-683 HB, 80-1042 HV, 30.6-102.6 HS 
• Accuracy: ± 0.5%, Repeatability: ± 0.6%
• Impactor: Type D
• USB and WiFi for data transmission
• Incl. ISO Calibration Certificate

The Metal Hardness Testing Durometer PCE-2600N is used wherever a fast hardness test has to be carried out. It is possible to use the durometer PCE-2600N to determine the surface hardness of many metals. The durometer PCE-2600N is especially suitable for quality or product inspection.

• Measurement according to Leeb Rebound method
• Measurement units: HLD, HRA, HRB, HRC, HB, HV, HS
• Measurement ranges: 170-960 HLD, 59.1-88 HRA, 3.5-101.7 HRB, 17.9-69.5 HRC, 19-683 HB, 80-1042 HV, 30.6-102.6 HS 
• Accuracy: ± 0.5%, Repeatability: ± 0.8%
• Impactor: DL
• Display: 128 x 64 OLED

The PCE-PFG Durometer is a handy, digital measuring device for measuring tensile and compressive forces. The Durometer offers a sampling rate of 500 Hz and various measurement options such as real-time measurement (RT), maximum value measurement (PEAK), configurable average value acquisition (Average) and automatic measurement storage of up to 100 measurements.

• Measuring range: 0 … 2000 N
• Resolution: 0.5 N
• Accuracy: ± 0.3% of the measuring range
• Memory for 100 measurements
• USB interface
• Graphic display

The Metal Hardness Testing Durometer PCE-2600N-ICA is used wherever a fast hardness test has to be carried out. It is possible to use the durometer PCE-2600N-ICA to determine the surface hardness of many metals. The durometer PCE-2600N-ICA is especially suitable for quality or product inspection.

• Measurement according to Leeb Rebound method
• Measurement units: HLD, HRA, HRB, HRC, HB, HV, HS
• Measurement ranges: 170-960 HLD, 59.1-88 HRA, 3.5-101.7 HRB, 17.9-69.5 HRC, 19-683 HB, 80-1042 HV, 30.6-102.6 HS 
• Accuracy: ± 0.5%, Repeatability: ± 0.8%
• Impactor: DL
• Display: 128 x 64 OLED
• Includes ISO calibration certificate

Due to its compact design, the PCE-2550 durometer is very easy to use for incoming and outgoing inspections. Due to the adjustable hardness scales, the durometer PCE-2550 is versatile.

• Measurement according to Leeb Rebound method
• Measurement units: HLD, HRA, HRB, HRC, HB, HV, HS
• Measurement ranges: 170-960 HLD, 59.1-88 HRA, 3.5-101.7 HRB, 17.9-69.5 HRC, 19-683 HB, 80-1042 HV, 30.6-102.6 HS 
• Accuracy: ± 0.4%, Repeatability: ± 0.6%
• Impact Device: Type D
• Measuring Direction: 360°
• Internal measured value memory