The simple design and an absolutely straightforward operation make it possible for the practitioner to use the adhesion tester as an instrument for daily adhesion tests. Using adhesive with rapid curing, the tests can be performed by the user in the shortest possible time.

• Breakout force: 200 kg
• Diameter of base dolly, mm: 15.1 (№ 1) and 19.5 (№ 2)
• Specific breakout force, MPa: Dolly №1 up to 10 MPa (100) Dolly  №2 up to 6 MPa (60)

• measurement range: 0 ... 500 N
• resolution: 0.1 N
• accuracy: ±0.05 % FS
• sampling rate: 2 ... 100 Hz
• traverse speed: 100 mm/min, 300 mm/min
• traverse distance: 150 mm 
• Measurable edge thickness: 0.4...3.5 mm
• Measurable board thickness: 10...64 mm
• graphical display
• data logger

• electronically controlled hydraulic pump
• various measuring head sizes available
• adjustable pulling speed, limit and holding time
• graphical measurement history
• memory in csv file format
• incl. 20 mm measuring heads
• standard(s): GB/T 5210, ASTM D4541/D7234, ISO 4624/16276-1

PCE-CPT 20 is a Adhesion Tester, or surface coating flexibility testing device, used for testing the formability, ductility, adhesion and elongation of paints, lacquers, varnishes, powder and protective coatings on sheet metal. Used in manufacturing production, paint shop and quality control applications, the Adhesion Tester aids in determining coating strength, durability and elasticity.

• Tests surface coatings on metal sheets 0.3 to 1.25 mm thick
• Provides a maximum depression force of 2500 N
• Offers a display resolution of 0.01 mm

• Evaluation of adhesion
• For thin, thick or tough coatings
• Large, non-slip grip
• Various blades selectable

• manually controlled hydraulic pump
• various measuring head sizes available
• memory in CSV file format
• incl. 20 mm measuring heads
• standard(s): GB/T 5210, ASTM D4541/D7234, ISO 4624/16276-1

• Evaluation of adhesion
• For thin, thick or tough coatings
• Large, non-slip grip
• Various blades selectable

The simple design and an absolutely straightforward operation make it possible for the practitioner to use the adhesion tester as an instrument for daily adhesion tests. Using adhesive with rapid curing, the tests can be performed by the user in the shortest possible time.

• Breakout force: 200 kg
• Diameter of base dolly, mm: 15.1 (№ 1) and 19.5 (№ 2)
• Specific breakout force, MPa: Dolly №1 up to 10 MPa (100) Dolly  №2 up to 6 MPa (60)

The Ultrasonic Contact Impedance (UCI) Metal Hardness Tester PCE-3500 has been designed for the non-destructive hardness measurement of metallic components. A 136° Vickers diamond at the probe is stimulated with its self-resonance to allow the user to very accurately measure hardness of small items, thin-walled items (>1 mm), and surface-hardened layers. Small imprint after measuring for mirrored surfaces and nitrided surfaces.

• Probe is 10 Newtons / 2.2 lbf force, 50 and 98 N probes are options
• Tests HRC, HRB, HV, HB, MPa
• Memory function via SD card and included PC software
• Large color LCD display with back lighting