PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable material hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable hardness tester or durometer that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys to measure on a minimum material thickness of 2 mm / .08 in. The test instrument can be mounted on a test stand (as an option) for series measurement in manufacturing process checking. Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
PCE-5000 is a portable hardness tester that uses the ASTM A1038 ultrasonic contact impedance (UCI) method to measure the hardness of metals and alloys with a minimum thickness of 2 mm / .08 in. Non-destructive testing produces microscopic indentation.
- Measurement according to ASTM A1038 ultrasonic contact impedance (UCI) method
- Measurement units: Rockwell A (HRA), Rockwell B (HRB), Rockwell C (HRC), Brinell (HB), Vickers (HV) and MPa (N/mm²) SI units
- Measurement ranges: 61-85.6 HRA, 41-100 HRB, 20.3-68 HRC, 85-650 HB, 50-999 HV, 255-2180 MPa (N/mm²)
- Accuracy: ± 1.5 HR, ± 3% HB, ± 3% HV, Repeatability: ± 0.3%
- Memory size: 1,000 groups for measurement data and 20 groups for calibration data
- Different probe types (also automatic motorized probes) available
The PCE-MM 800 microscope is designed to display simple magnifications on a computer screen. For this purpose, the PCE-MM 800 microscope is connected to a screen. This allows a large presentation visible by several people.
- 200 ... 1600-times magnification
- Bright LED lighting
- Maximum display: 1600 x 1200 pixels
- USB interface
- Digital zoom
PCE-MM 200UV is a UV USB microscope, or UV USB inspection camera, that magnifies objects up to 200 times. This Videoscope uses 8 UV LEDs with a wavelength of 400 nm for illumination. The microscope captures photos and videos as well as displays magnified objects in real time on your computer screen.
- Magnification: Continuous, 10 ... 200 times (infinitely variable)
- Resolution: 1600 x 1200 pixels
- Colors: 24-bit RGB
PCE-CPT 20 is a Adhesion Tester, or surface coating flexibility testing device, used for testing the formability, ductility, adhesion and elongation of paints, lacquers, varnishes, powder and protective coatings on sheet metal. Used in manufacturing production, paint shop and quality control applications, the Adhesion Tester aids in determining coating strength, durability and elasticity.
- Tests surface coatings on metal sheets 0.3 to 1.25 mm thick
- Provides a maximum depression force of 2500 N
- Offers a display resolution of 0.01 mm
PCE-CPT 20 is a Material Tester, or surface coating flexibility testing device, used for testing the formability, ductility, adhesion and elongation of paints, lacquers, varnishes, powder and protective coatings on sheet metal. Used in manufacturing production, paint shop and quality control applications, the Material Tester aids in determining coating strength, durability and elasticity.
- Tests surface coatings on metal sheets 0.3 to 1.25 mm thick
- Provides a maximum depression force of 2500 N
- Offers a display resolution of 0.01 mm